奇美 POLYLAC® MABS 樹脂是一種共聚物，主要由甲基丙烯酸甲酯 (MMA)、丙烯腈 (AN)、丁二烯 (BD) 及苯乙烯 (SM) 組成，提供良好的透明度、加工性、機械性質及尺寸安定性。. 我們為了實現頂尖的透明度，調整 ABS 及橡膠基質的折射率使其一致。. MABS 也具備高耐衝擊性 ...
物性表. POLYLAC® PA-757. 丙烯腈丁二烯苯乙烯. CHI MEI CORPORATION. 产品说明. POLYLAC® PA-757 是一种丙烯腈丁二烯苯乙烯(ABS) 产品,. 它可以通过注射成型进行加工, 在北美洲, 非洲和中东, 拉丁美洲, 欧洲或亚太地区有供货.特性包括:阻燃/额定火焰通过 ROHS 认证. 物理性能. 额定值. 单位制. 测试方法. 比重. 机械性能. 额定值. 单位制. 测试方法. 拉伸应力. 伸长率. 弯曲模量 6.00 mm 3. 2650. MPa. ASTM D790. -- 4. 2200. MPa. ISO 178 弯曲强度. 悬壁梁缺口冲击强度. 热性能. 额定值. 单位制. 测试方法. 载荷下热变形温度. 维卡软化温度. 可燃性.
Chi Mei Polylac® PA-757 ABS. Category : Polymer , Thermoplastic , ABS Polymer , Acrylonitrile Butadiene Styrene (ABS), Molded. Material Notes: High gloss, medium impact. Order this product through the following link: http://www.lookpolymers.com/polymer_Chi-Mei-Polylac-PA-757-ABS.php. Physical Properties.
產品敘述: High gloss, Medium impact,black. 物性ISO 測試方法 測試條件 單位 PA-757 J01 熔融指數1133 220℃×10KG ml/10 min 17 比重1183 23 ℃ g/cm31.05 拉伸強度527. 50 mm/min, yield MPa 47 50 mm/min, break MPa 35 延伸率527 50 mm/min % 50 彎曲強度. 178. 2 mm/min MPa 70 彎曲彈性模數 2 mm/min GPa 2.4. IZOD ...
奇美電商App 透過奇美實業APP，便一手掌握最新、最完整的各項材料相關資訊，奇美不僅能提供夥伴高性能的材料，同時也能成為最強力的數位支援！
2020年8月21日 · POLYLAC® PA-757 is an Acrylonitrile Butadiene Styrene (ABS) product. It is available in Africa & Middle East, Asia Pacific, Europe, Latin America, or North America. Characteristics include: Flame Rated. RoHS Compliant. High Gloss. Impact Resistant. General. Material Status. Literature 1. UL Yellow Card 2. Search for UL Yellow Card. E56070-565071.
Chi Mei Polylac® PA-757 ABS. Categories: Polymer; Thermoplastic; ABS Polymer; Acrylonitrile Butadiene Styrene (ABS), Molded. Material Notes: High gloss, medium impact. Vendors:
The above statement is based on our current level of knowledge and covers the above products directly manufactured and supplied by CHI MEI CORPORATION at the date of issue. CHI MEI CORPORATION makes no warranties, whether express or implied, and
General ABS POLYLAC®PA-757. Product Description: High gloss, Medium impact. Properties ISO Test Method Test Condition Unit PA-757 Melt Flow Index 1133 220℃×10KG ml/10 min 19 Mass Density 1183 23 ℃ g/cm31.05 Tensile Strength 527. 50 mm/min, yield MPa 47 50 mm/min, break MPa 34 Tensile Elongation 527 50 mm/min % 70 Flexural Strength.
CHI MEI CORPORATION 59-1 SAN CHIA, JEN TE, TAINAN COUNTY, TAIWAN R.O.C. TEL: 886-6-266-5000, FAX: 886-6-266-5555~7 泛用級 ABS, POLYLAC® PA-757 V1W 材料特性 特性(Properties) 測試方法(Test Method) 測試條件(Test Condition